SR 1500 - Laminating Sicomin

This modified epoxy resin has been formulated to be cristalization free and low toxicity. This epoxy system has very good wet-out, degazing properties and an excellent adhesion to all type of reinforcements ( glass, aramid, carbon, polyester…)

Adjustable working time depending on the choice of the hardener Respecting the ratio resin / hardener, the hardeners are mixable by weight, to achieve the most adapted reactivity for the application.

Glass transition : 75 - 81°C The parts can be in service after 7 to 14 days at 23°C for the hardeners SD 2507, SD 2806, SD 2505 and SD 2503.
Post-cure at a minimum of 40°C for a Tg above 55°C
Developped for : ship building, aeronautic, automotive prototypes, tool making.
Other applications : putty for coating with microspheres, syntactic core material, casting volume depending on the hardeners.

Typical use SR 1500 / SD 2507, SD 2806 : Low thickness laminates, low temperature hardening (10 - 15°C). Rapid repair and bonding, putty…

SR 1500 / SD 2505 , SD 2503: Standard lamination system, all dimension parts, tooling, fillet joint…

SR 1500 / SD 7561 Big parts, or high thickness laminate parts. Injection, infusion, casting… Long open time with laminate. Post curing temperature : 55 °C minimum